DK 180 Thick Polyaspartic Clear Coating - 1 Gallon Kit - Gloss
DK 180 Thick Polyaspartic Clear Coating - 1 Gallon Kit - Gloss is backordered and will ship as soon as it is back in stock.
Couldn't load pickup availability
DK-180 is a specially formulated 80% solids hybrid solvent based polyaspartic coating. Unlike many polyaspartics, it has a user-friendly pot life of approximately 20 minutes and the ability to create a moderate build (6 ½ mil) single coat top coat. Turnaround time for a floor may be as little as 6 – 8 hours. Epoxy flakes may be covered in a single pass.
Dura- Kote DK-180 provides a low VOC (less than 200 g/L), UV stable, penetrating, film forming, color enhancing, and high gloss, moderate build wear surface. The rapid cure time eliminates excessive waiting to return a floor to service. It is ideally suited for both commercial and residential settings: aircraft hangars, clean room floors, manufacturing facilities, warehouses, bars, clubs, retail stores, automotive showrooms, residential interiors, garage floors, stadiums, or any high traffic area where an exceedingly resilient floor is desired.
Surecrete DuraKote DK-180 Specs
- VOC Rating – less than 200 g/L
- Solids Content – 80%
- Pot Life – approximately 20 minutes
- Shelf Life – 1 year in original unopened container
- Ready for re-coat – Approximately 2 hours (6-8 hours at low temperatures)
- Light Duty Use – 4-6 hours (Up to 24 hours at low temperatures)
- Heavy Traffic Ready – Approximately 24 hours (Up to 3 days at low temperatures)
- Full Cure – 1-2 days (Up to 7 days at low temperatures)
- Appearance (cured) – Clear Gloss
- Appearance (wet) – Clear
- Water Resistance – Excellent, beads water
- Mechanical Stability – Excellent
- Light Stability – Excellent
- Odor – Aromatic
- Application Temperature – 32 – 90 degrees Fahrenheit
- Gardener direct / Reverse impact – More than 160 inch pounds
- Taber Abrasion – 40-60 mg loss
- Gloss Retention – More than 95% at 2,000 hours
Coverage
Approximately 150-200 square feet per gallon, per coat (varies widely based on substrate porosity and application methods)